구현 표준: 구조용 GB/T8162 이음매 없는 강관, 유체 운송용 GB/T8163 이음매 없는 강관. 0420D 및 0420E 기계적 성질: 인장강도 520~680MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
파이프 제조 방법: 파이프는 연속 주조, 금형 주조 또는 열간 압연으로 제조할 수도 있습니다.
연속주조관은 YB/T 4149의 규정도 준수해야 합니다. 뜨거운 파이프는 YB/T 5221 또는 YB/T 5222의 규정도 준수해야 합니다. 몰드 캐스트 파이프는 뜨거운(단조) 파이프의 규정을 참조할 수도 있습니다.